Vacuum pressure sintering furnace

Vacuum pressure sintering furnace

In vacuum pressure sintering furnace this equipment, sintering material under high temperature is also subject to mechanical stress and the effect of vacuum, can be used in the sintering density after casting products. General powder material filling in the graphite mold, mechanical pressure by 700-1500 mn/m3, and heated to 2500 ℃ in the vacuum. Mold by direct current heating, indirect heating.
Vacuum pressure sintering furnace is mainly used for sintering is the density of the material with high temperature gas reactions billet, such as oxide, carbide and boride gas after sintering material can reach very high density, general density is greater than the theoretical value of 95%, and with high purity. Graphite resistor and graphite mould in the vacuum operation of weight loss is minimal. Vacuum hot pressing sintering is at the same time in the compaction process and utilization of high pressure, temperature and time, and many other parameters to control the quality of the sintered body.